Hope you are fine.We are from ZHEJIANG HENGTAIYUAN PU CO., LTD.Our company is the professional manufacturer of polyurethane and iso for shoe sole making in China,it was established in 2003. Our products are divided into PU resin for shoe sole, polyes

牌号(Shop sign):ZG-P-8086D/ZG-I-9823

 

  1. 特性:超高硬度,超低密度鞋底

 Characteristics:Super high hardness, super low density PU resin for shoe sole.

  1. 用途:适用于女士高跟及坡跟鞋的生产

Application:Applicable for the production of women's high heel and wedge shoe sole.

  1. 原液特性Typical properties of PU Resin

品   名

Name of products

外   观

Appearance

粘   度

Viscosity

(Pa·s/50℃)

密   度

Density

(g/cm3/40℃)

包  装

Package

(kg)

ZG-P-8086D

白色或淡黄,液状无异物

White or pale yellow, liquid, no foreign material

0.30-0.60

1.16-1.20

18

ZG-I-9823

透明液体无异物

Transparent liquid, no foreign material

0.05-0.20

1.18-1.20

20

参考发货配比(Reference shipments ratio):A/B=30/25(桶)

Reference shipments ratio: A/B=30/25(barrel)

  1. 催化剂与辅助剂Catalysts and auxiliary agents:

   ZG-P-8086D/ZG-AC-2/水 =18kg/230-300/70-120g 注:辅助剂的加入在不同地区和不同环境及不同生产条件作相应调整。

ZG-P-8086D/ZG-AC-2/water =18kg/230-300g/70-120g Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.

  1. 成型条件及物性值(Molding conditions & physical properties):

反应性

Reactivity

技术指标

Technical index

测试项目

Test item

参考物性值

Reference physical properties

参考配比

Reference ratio

P+C/I  

100/106-108

鞋底成型密度

Molded density of sole

(g/cm3

0.28-0.35

使用温度

Using temperature(℃)

A料:45-50;B料:38-42

A material: 45-50; B material:38-42

硬度(A型)

Hardness (type A)

65-85

乳白时间

Cream time(s)

5-9

拉伸强度

Tensile strength(MPa)

6.0-8.0

升起时间

Rise time(s)

30-45

伸长率

Elongation(%)

----

金属模具温度

Metal mold temperature

(℃)

45-55

DIN耐磨

DIN abrasion resistance(mm3

----

脱模时间

Demould time

(min)

2.5-4

自由泡密度

Free foam density

(g/cm3

0.12-0.16

 

 

耐折性(常温)

(4万次裂口长度,mm)

Folding endurance (room temperature)

(40,000 gap length mm)

<8

Type:
Manufacturer
Established:
2003
Employees:
250
Keywords:

pu for shoe sole

BUSINESS REVIEWS

Add new review

There are no reviews at the moment

Contact Persons

Tradezone.com

Tradezone.com has been putting suppliers and buyers together for over 65 years.  This Suppliers Directory focuses on promoting International Trade.  You are welcome to list your company and products here and we will do our best to provide great internet exposure for you.

 

Copyright © 2020 Tradezone.com. All Rights Reserved

Search